Thread: Powder coating frame versus painting.

Tweet

i can not see why you could not fill pits with EZ grind mig wire i did this alot on body steel on door edges were filler would chip off or brass filler rod i would try out your tig ? i think you would not have to deal with the glass fluxs from a torch set or use the low melting filler rod muggy sales or the like lead filler eastwood has if you have need to do some fill. i have been told that some of the filler will gas out from the heat this could do with if it is thin steel or thick ?.i have work out steel with no filler if its not to bad you can fill and work out the steel with a body file and steel files use some chalk to rub in to the file stop the file from pluging up a 8 inch soft pad with 80 grit and then a da with a 6 inch pad 80to120 .the frame can be guide coated to see were you need to work the steel i do not use flap wheels they will not get any thing dead flat hope this help don